Rongsheng High Temperature Alumina Magnesia Carbon Refractory Bricks For Induction Furnace Ladle Arc Furnace Linings

Name: Rongsheng High Temperature Alumina Magnesia Carbon Refractory Bricks For Induction Furnace Ladle Arc Furnace Linings
Brand: RONGSHENG
Price: 1 USD

$Quality Rongsheng High Temperature Alumina Magnesia Carbon Refractory Bricks For Induction Furnace Ladle Arc Furnace Linings for sale$ $Quality Rongsheng High Temperature Alumina Magnesia Carbon Refractory Bricks For Induction Furnace Ladle Arc Furnace Linings for sale$ $Quality Rongsheng High Temperature Alumina Magnesia Carbon Refractory Bricks For Induction Furnace Ladle Arc Furnace Linings for sale$ $Quality Rongsheng High Temperature Alumina Magnesia Carbon Refractory Bricks For Induction Furnace Ladle Arc Furnace Linings for sale$

Brand Name : RONGSHENG

Certification : ISO9001

Place of Origin : Henan, China

Material : Fireclay, Alumina, Silica, Magnesite, or Mullite

Apparent Orosity : ≤22%

Chemical Composition : Al2O3-SiO2

Transportation : Shipping

Cold Crushing Mpa : 350

Servicelife : Typically 3-10 years depending on operating conditions

Chemical Resistance : Excellent

Diameter : 200mm-800mm

Thermal Shock Resistance : ≥20 times

Use : lime kiln and other kiln project

Installation Method : Vibration

Shape : Rectangular, Modular, or Special shapes

Size : 230 x 114 x 65 mm (standard) or customized

Aluminum Content : ≥70%

Sizedimensions : 230 x 114 x 65 mm (standard)

Contact Now

Key attributes

Refractoriness (Degree)

High Refractory (1770 °C~2000 °C)

Material

MgO-Carbon Brick

Shape

Brick

Processing Service

Bending, Cutting, Moulding

Al2O3 Content (%)

Customizable

CaO Content (%)

8%-14%

CrO Content (%)

0.002%

MgO Content (%)

72%-84%

SiC Content (%)

1.2-1.4%

SiO2 Content (%)

little

Place of Origin

Henan, China

Brand Name

Rongsheng

Product name

Alumina Magnesia Carbon Bricks

Bulk density

≥2.77g/cm3

Cold crushing strength(mpa)

≥25 Mpa

Working temperature

1800 Degree Celsius

Keyword

Magnesia Carbon Refractory Bricks

Application

Steel Making Furnace Lining

Size

230mm*114mm*65/75mm or other sizes

Advantage

Erosion Resistance

Feature

Great performance to anti-slag

Certificate

ISO9001 / CE

Packaging and delivery

Selling Units

Single item

Single package size

30X10X10 cm

Single gross weight

3.000 kg

Magnesia carbon bricks are made from high melting point alkaline oxide magnesium oxide (melting point 2800 ℃) and high melting point carbon materials that are difficult to be infiltrated by slag, with various non oxide additives added. A unburned carbon composite refractory material formed by combining carbon based binders.

Magnesia Carbon bricks are very mature product in our area. As our area has 1/4 world storage of best quality Magnesia ore, we can provide as good quality as European Mg-C bricks with competitive prices. We also provide basic refractory lining solution for CONVERTER, EAF, LF, LADLE, etc. these industrial furnaces.